Abstract
High-density ceramics of ceria doped with 0, 3, 5, 10, 15 and 20 mol.% Gd and with grain sizes exceeding 1.5 μm were investigated by nanoindentation. The deduced elastic moduli are independent of Gd content and remain close to the value reported for bulk ceramics (210 ± 5% GPa). All ceramics exhibit transient creep with displacement proportional to the 1/3 power of the time. For 0.05 < x < 0.2, the derived creep magnitude parameter decreases linearly with increasing Gd content. These results strongly suggest that defect rearrangement influences the measurements.
Original language | English |
---|---|
Pages (from-to) | 155-158 |
Number of pages | 4 |
Journal | Scripta Materialia |
Volume | 66 |
Issue number | 3-4 |
DOIs | |
State | Published - Feb 2012 |
Externally published | Yes |
Keywords
- Creep rate
- Elastic modulus
- Gd-doped ceria
- Nanoindentation