TY - JOUR
T1 - Low temperature synthesis of Hg1-xCdxTe, 0 ≤ x ≤ 1
AU - Ben-Dor, L.
AU - Yellin, N.
AU - Shaham, H.
PY - 1983/10
Y1 - 1983/10
N2 - Solid solutions of Hg1-xCdxTe with 0 ≤ x ≤ 1.0 were prepared at low temperatures, where Hg pressure is about 1 atm. For the composition x < 0.7, complete reaction was observed within 72 h at 420°C. For x = 0.7, 0.9 and 1.0, minimum synthesis temperatures of 460°C, 490°C and 760°C, respectively, were needed for complete reaction. Homogeneous solid solutions of Hg1-xCdxTe, as determined by X-ray and atomic absorption analyses, were obtained after 168 h at 420°C for x < 0.7, the temperature increasing for x ≥ 0.7.
AB - Solid solutions of Hg1-xCdxTe with 0 ≤ x ≤ 1.0 were prepared at low temperatures, where Hg pressure is about 1 atm. For the composition x < 0.7, complete reaction was observed within 72 h at 420°C. For x = 0.7, 0.9 and 1.0, minimum synthesis temperatures of 460°C, 490°C and 760°C, respectively, were needed for complete reaction. Homogeneous solid solutions of Hg1-xCdxTe, as determined by X-ray and atomic absorption analyses, were obtained after 168 h at 420°C for x < 0.7, the temperature increasing for x ≥ 0.7.
UR - http://www.scopus.com/inward/record.url?scp=0020832450&partnerID=8YFLogxK
U2 - 10.1016/0025-5408(83)90026-0
DO - 10.1016/0025-5408(83)90026-0
M3 - ???researchoutput.researchoutputtypes.contributiontojournal.article???
AN - SCOPUS:0020832450
SN - 0025-5408
VL - 18
SP - 1229
EP - 1233
JO - Materials Research Bulletin
JF - Materials Research Bulletin
IS - 10
ER -